NFM31HK104R1H3_ (1206, 0.1uf, dc50v) _: packaging code reference sheet 1.scope 2.murata part no. system (ex.) 3. type & dimensions a)equivalent circuit (unit:mm) 4.rated value 5.package product specifications in this catalog are as of feb.9,2016,and are subject to change or obsolescence without notice. please consult the approval sheet before ordering. please read rating and !cautions first. chip emifil?chip 3-terminal capacitor for very large current for automotive specifications and test methods (operating /storage temp. range) -55 to 125 c / -55 to 125 c 20 % 6a(dc) 3.0mmax. 0.1 uf mark packaging unit (7) packaging i 1.20.3 j 0.30.2 this product specification is applied to chip emifil?chip 3-terminal capacitor for very large current used for automotive electronic equipment. (3) nominal capacitance capacitance tolerance (5) dc rated voltage rated current (ma) dc resistance 1000mmin. dc 50 v insulation resistance (1)-1 l (1)-2 w t e g l f 180mm reel embossed w8p4 3000 pcs./reel 3.20.2 1.60.2 1.30.2 0.40.3 0.3 min. (1)l/w dimensions (2)features (3)nominal capacitance (4) characteristics (5)dc rated voltage (6)electrode (7)packaging code NFM31HK104R1H3-01 1 nfm 31 hk 104 r 1h 3 l
aec-q200 murata standard specification and test methods electrical performance no specification test method 1 capacitance shown in rated value. frequency: 10.1khz (cap.) voltage : 10.2v(rms) 2 voltage : rated voltage time : 2 minutes max. 3 dc resistance measured with 100ma max. 4 withstanding voltage products shall not be damaged. test voltage : rated voltage x 300% time : 1 to 5 s charge current : 50 ma max. 5 operating temperature shown in rated value. self-temperature rise is not included 6 storage temperature standard testing condition < unless otherwise specified > < in case of doubt > temperature : ordinary temp. / 15 c to 35 c temperature: 20 c 2 c humidity: ordinary humidity / 25 %(rh) to 85 %(rh) humidity: 60 %(rh) to 70 %(rh) atmospheric pressure: 86 kpa to 106 kpa item insulation resistance(i.r.) jemcps-02916 2
aec-q200 murata standard specification and test methods mechanical performance (based on table 2 for tantalum & ceramic capacitors) aec-q200 rev.d issued june 1. 2010 murata specification / deviation no. stress test method 3 high temperature exposure unpowered 1000 hours @ maximum operating temperature(ceramics) measurement at 24+/-2 hours after test meet table d after testing. 4 temperature cycling 1000cycles (-55c to +125c) measurement at 24+/-2 hours after test meet table a after testing. 7 biased humidity 1000hours 85c/85%rh. note: ceramics only specified conditions: rated voltage and 1.3 to 1.5 volts. add 100kohm resister. tantalums-rated voltage only. measurement at 24+/-2 hours after test meet table d after testing. 8 operational life condition d steady state ta=125c full rated ceramic caps measurement at 24+/-2 hours after test conclusion. meet table d after testing. 9 external visual visual inspection no abnormalities 10 physical dimension meet item 4 type & dimensions no defects 12 resistance to solvents per mil-std-202 method 215 not applicable 13 mechanical shock figure 1 of method 213. smd:condition f leaded:condition c meet table c after testing. 14 vibration 5g's for 20 minutes, 12cycles each of 3 oritentations use 8"x5" pcb, .031"thick. 7 secure points on one long side and 2 secure points at corners of opposite sides. parts mounted within 2" from any secure point. test from 10-2000hz. meet table c after testing. 15 resistance to soldering heat no pre-heat of samples. note: test condition d for smd. test condition b for leaded. pre-heat condition of 150oc, 60-120sec is allowed for ceramic components. meet table a after testing. deviation for aec-q200; testing condition flux: ethanol solution of rosin, 25(wt)% pre-heating: 150c+/-10c, 60 to 90s solder: sn-3.0ag-0.5cu solder temperature: 270c+/-5c immesion time: 10s+/-1s immesion and emersion rates: 25mm/s then measured after exposure in the room. 17 esd per aec-q200-002 component classification:meet table e 18 solderability per j-std-002 95% of the terminations is to be soldered. method b : not applicable 19 electrical characterization summary to show min, max, mean and standard deviation at room as well as min and max operating temperatures. deviation for aec-q200; shown in rated value. aec-q200 jemcps-02916 3 4 5 r 3 4 0 f d e f l e c t i o n 4 5 p r o d u c t p r e s s u r e j i g
aec-q200 murata standard specification and test methods mechanical performance (based on table 2 for tantalum & ceramic capacitors) aec-q200 rev.d issued june 1. 2010 murata specification / deviation no. stress test method 21 board flex required for mlccs only. 60 sec minimum holding time. meet table b after testing. deviation for aec-q200; it shall be soldered on the glass-epoxy substrate (100 401.0mm). ? deflection : 1mm ? keeping time : 30s 22 terminal strength per aec-q200-006 a force of 17.7n for 60 s the electrode should show no failure after testing. deviation for aec-q200; it shall be soldered on the substrate. ? applying force : 9.8n ? applying time : 30s 23 beam load test per aec-q200-003 the chip endure 14.7n. deviation for aec-q200 place the capacitor in the beam load fixture as below figure. pressure jig: r0.5 speed supplied the stress load : 0.5m/s aec-q200 iron board jemcps-02916 4 4 5 r 3 4 0 f d e f l e c t i o n 4 5 p r o d u c t p r e s s u r e j i g
aec-q200 murata standard specification and test methods mechanical performance (based on table 2 for tantalum & ceramic capacitors) aec-q200 rev.d issued june 1. 2010 table a appearance no damage capacitance change within +/-7.5% i.r. meet initial value shown in rated value.) dc resistance 0.05 max. tabe b appearance no damage capacitance change within +/-7.5% dc resistance 0.05 max. table c appearance no damage capacitance meet initial value shown in rated value.) dc resistance 0.05 max. table d appearance no damage capacitance change within +/-12.5% i.r. 50m min. dc resistance 0.05 max. table e murata pn dc resistance value after testing () max. esd component classification 1c: 1kv(dc) to 2kv(dc) nfm31hk series 0.05 1c jemcps-02916 5
1. appearance and dimensions (8mm-wide plastic tape) (in mm) 2. specification of taping (1) packing quantity (standard quantity) 3000 pcs. / reel (2) packing method products shall be packaged in the cavity of plastic tape and sealed cover tape. (3) sprocket hole the sprocket holes are to the right as the tape is pulled toward the user. (4)cover tape cover tape has no spliced point. (5) missing components number 3. pull strength of plastic tape and cover tape 4. peeling off force of cover tape 0.2n to 0.7n (minimum value is typical) speed of peeling off : 300 mm / min 5. dimensions of leader-tape, trailer and reel there shall be leader-tape (cover tape only and empty tape) and trailer-tape (empty tape) as follows. (in mm) p a c k a g i n g nfm31 type missing components number within 0.1% of the number per reel or 1 pc., whichever is greater,and are not continuous. the specified quantity per reel is kept. dimension of the cavity is measured at the bottom jemcpp-02233a 6 e m p t y t a p e 1 9 0 m i n . l e a d e r t r a i l e r t o p t a p e 2 . 0 0 . 5 f 1 3 . 0 0 . 2 f 2 1 . 0 0 . 8 f 1 8 0 f 6 0 9 1 3 1 . 4 1 0 0 3 d i r e c t i o n o f f e e d 2 1 0 m i n . 1 6 0 m i n . 1 0 l a b e l plastic tape 5n min. cover tape 10n min .
1.operating environment do not use this product under the following environmental conditions, on deterioration of the performance, such as insulation resistance may result from the use. (1) in the corrodible atmosphere (acidic gases, alkaline gases, chlorine, sulfur gases, organic gases and etc.) (2) in the atmosphere where liquid such as organic solvent, may splash on the products. (3) in the atmosphere where dust rises. (4) in the atmosphere where the temperature / humidity changes rapidly and it is easy to dew 2. caution (rating) do not use products beyond the operating temperature range, rated voltage and rated current. 3. attention regarding product's lay out < attention regarding the heat generated by other products > please provide special attention when mounting products in close proximity to other products that radiate heat. 4. attention regarding chip mounting an excessively low bottom dead point of the suction nozzle imposes great force on the chip during mounting, causing cracked chips. please set the suction nozzle's bottom dead point on the upper surface of the board, after the board is adjusted flat. the chip received force (static loading) from the suction nozzle's should be 1n to 3n. 5. note for assembling < thermal shock > pre-heating should be in such a way that the temperature difference between solder and products surface is limited to 100c max. also cooling into solvent after soldering should be in such a way that the temperature difference is limited to 100c max. 6. attention regarding p.c.b. bending the following shall be considered when designing p.c.b.'s and laying out products. (1) p.c.b. shall be designed so that products are not subject to the mechanical stress for board warpage. [products direction] products shall be located in the sideways direction (length:ac >b P d. caution ! jemcpc-02252a 7 p o o r e x a m p l e g o o d e x a m p l e b a s e a m s l i t a d b c b a l e n g t h : a ? b
7. pre-heating temperature soldering shall be handled so that the difference between pre-heating temperature and solder temperature shall be limited to 100c max. to avoid the heat stress for the products. ? standard printing pattern of solder paste. 8. reflow soldering 1) soldering paste printing for reflow ? standard thickness of solder paste: 100m to 150m. ? use the solder paste printing pattern of the right pattern. ? for the resist and copper foil pattern, use standard land dimensions. 2) soldering conditions (in mm) standard soldering profile and the limit soldering profile is as follows. the excessive limit soldering conditions may cause leaching of the electrode and/or resulting in the deterioration of product quality. 1) printing of adhesive adhesive amount shall be about 0.06mg per chip to obtain enough adhesive strength. the adhesive position is as follows 2)standard soldering profile and the limit soldering profile is as follows. the excessive limit soldering conditions may cause leaching of the electrode and/or resulting in the deterioration of caution 9. flow soldering product quality. ! jemcpc-02252a 8 4 . 4 1 . 0 2 . 5 1 . 2 2 . 6 0 . 6 a d h e s i v e p o s i t i o n o f a d h e s i v e standard profile l imit profile pre - heating 150 c ~ 180 c , 90s 30s heating above 220c , 30s ~ 60s above 230 c , 60s max. peak temperature 245c 3c 260 c , 10s cycle of reflow 2 times 2 times l i m i t p r o f i l e s t a n d a r d p r o f i l e 9 0 s 3 0 s 2 3 0 c 2 6 0 c 2 4 5 c 3 c 2 2 0 c 3 0 s 6 0 s 6 0 s m a x . 1 8 0 1 5 0 t e m p . t i m e . ( s ) ( c ) 2 6 5 c 3 c 2 5 0 c 6 0 s m i n . 1 5 0 l i m i t p r o f i l e t i m e . ( s ) ( c ) t e m p . h e a t i n g t i m e s t a n d a r d p r o f i l e standard profile limit profile pre - heating 150 c , 60s min. heating 250 c , 4s ~ 6s 265 c 3 c, 5s max. cycle of reflow 2 times 2 times
10. reworking with soldering iron the following conditions shall be strictly followed when using a soldering iron. ? pre-heating : 150c, 1 minute ? soldering iron output : 30w max. ? tip temperature : 350c max. ? tip diameter : 3mm max. ? soldering time : 3(+1,-0) s ? times : 2times max. note: do not directly touch the products with the tip of the soldering iron in order to prevent the crack on the ceramic material due to the thermal shock. 11. solder volume solder shall be used not to be exceeded as shown below. accordingly increasing the solder volume, the mechanical stress to product is also increased. excessive solder volume may cause the failure of mechanical or electrical performance. 12.resin coating the capacitance value may change and/or it may affect on the product's performance due to high cure-stress of resin to be used for coating / molding products. so please pay your careful attention when you select resin. in prior to use, please make the reliability evaluation with the product mounted in your application set. 13. handling of a substrate after mounting products on a substrate, do not apply any stress to the product caused by bending or twisting to the substrate when cropping the substrate, inserting and removing a connector from the substrate or tightening screw to the substrate. excessive mechanical stress may cause cracking in the product. bending twisting failure to follow the above cautions may result, worst case, in a short circuit and cause fuming or partial dispersion when the product is used. 14.fail-safe be sure to provide an appropriate fail-safe function on your product to prevent a second damage that may be caused by the abnormal function or the failure of our product. 15.limitation of applications (1)aircraft equipment (2)aerospace equipment (3)undersea equipment (4)power plant control equipment (5)medical equipment (6)transportation equipment(trains, ships, etc.) (7)traffic signal equipment (8)disaster prevention / crime prevention equipment (9)data-processing equipment (10)applications of similar complexity or with reliability requirements comparable to the applications listed in the above caution please contact us before using our products for the applications listed below which require especially high reliability for the prevention of defects which might directly cause damage to the third party's life, body or property. ! jemcpc-02252a 9 u p p e r l i m i t r e c o m m e n d a b l e 1 / 3 t ? t ? t ( t : c h i p t h i c k n e s s ) t r e c o m m e n d a b l e u p p e r l i m i t
this product is designed for solder mounting. please consult us in advance for applying other mounting method such as conductive adhesive. 1. flux and solder 2. cleaning conditions products shall be cleaned on the following conditions. (1) cleaning temperature shall be limited to 60c max. (40c max. for isopropyl alcohol (ipa)) (2) ultrasonic cleaning shall comply with the following conditions, with avoiding the resonance phenomenon at the mounted products and p.c.b. power : 20w / l max. frequency : 28khz to 40khz time : 5 minutes max. (3) cleaner 1. cleaner isopropyl alcohol (ipa) 2. aqueous agent pine alpha st-100s (4) there shall be no residual flux and residual cleaner after cleaning. in the case of using aqueous agent, products shall be dried completely after rinse with de-ionized water in order to remove the cleaner. (5) other cleaning please contact us. 3. standard land dimensions the chip emi filter suppresses noise by conducting the high-frequency noise element to ground. < standard land dimensions for reflow > < standard land dimensions for flow > ?side on which chips are mounted ?side on which chips are mounted (in mm) 4.storage and delivery condition (1) storage period use the products within 12 months after delivered. solderability should be checked if this period is exceeded. (2) storage environment condition ? products should be stored in the warehouse on the following conditions. temperature: -10 to +40c humidity: 15 to 85% relative humidity no rapid change on temperature and humidity ? dont keep products in salty breeze, corrosive gases such as sulfur, chlorine gas or acid, or it may cause oxidization of electrode, resulting in poor solderability. ? products should be stored on the palette for the prevention of the influence from humidity, dust and so on. ? products should be stored in the warehouse without heat shock, vibration, direct sunlight and so on. ? products should be stored under the airtight packaged condition. (3) delivery care should be taken when transporting or handling product to avoid excessive vibration or mechanical shock. notice therefore, to get enough noise reduction, feed through holes which is connected to ground-plane should be arranged according to the figure to reinforce the ground-pattern. for large current design, width of signal land pattern should be wider not less than 1mm per 1a (1mm/a) for example in case of 10a, signal land pattern width should be 10mm or more. (1mm/a *10a= 10mm) jemcpc-02252a 10 small diameter thru hole 0.4 1.0 1.4 2.5 4.4 0.6 1.2 2.6 3.0 10mm or more (in case of 10a) resist small diameter thru hole 0.4 copper foil pattern 1.0 1.4 2.5 4.4 0.6 1.2 2.6 3.0 10mm or more (in case of 10a) no pattern flux use rosin - based flux, do not use highly acidic flux (with chlorine content exceeding 0.2(wt)%). do not use water - soluble flux. other flux (except above) please contact us for details, then use. solder use sn - 3.0ag - 0.5cu solder use of sn - zn based sold er will deteriorate performance of products. in case of using sn - zn based solder, please contact murata in advance.
(1) please make sure that your product has been evaluated in view of your specifications with our product being mounted to your product. (2) you are requested not to use our product deviating from the agreed specifications. (3) we consider it not appropriate to include any terms and conditions with regard to the business transaction in the product specifications, drawings or other technical documents. therefore, if your technical documents as above include such terms and conditions such as warranty clause, product liability clause, or intellectual property infringement liability clause, they will be deemed to be invalid. note ! jemcpc-02252a 11

▲Up To Search▲

Price & Availability of NFM31HK104R1H3

	To Download NFM31HK104R1H3 Datasheet File
If you can't view the Datasheet, Please click here to try to view without PDF Reader .